Latamid 66 E21 G/15Polyamide 66LATI S.p.A.15% 玻璃纖維增強(qiáng)材料產(chǎn)品說明：Compound based on Polyamide 66 (PA 66).Toughened. Glass fibres.物理性能額定值單位制測(cè)試方法密度1.14g/cm3ISO 1183收縮率 1ISO 294-4    垂直流動(dòng)方向 : 2.00 mm1.0 到 1.3%ISO 294-4    流動(dòng)方向 : 2.00 mm0.50 到 0.80%ISO 294-4機(jī)械性能額定值單位制測(cè)試方法拉伸模量ISO 527-2/1    23°C4800MPaISO 527-2/1    60°C3400MPaISO 527-2/1    90°C2500MPaISO 527-2/1    120°C1900MPaISO 527-2/1    150°C1700MPaISO 527-2/1拉伸應(yīng)力ISO 527-2/5    屈服, 23°C95.0MPaISO 527-2/5    屈服, 60°C70.0MPaISO 527-2/5    屈服, 90°C55.0MPaISO 527-2/5    屈服, 120°C45.0MPaISO 527-2/5    屈服, 150°C35.0MPaISO 527-2/5    斷裂, 23°C90.0MPaISO 527-2/5    斷裂, 60°C65.0MPaISO 527-2/5    斷裂, 90°C45.0MPaISO 527-2/5    斷裂, 120°C35.0MPaISO 527-2/5    斷裂, 150°C30.0MPaISO 527-2/5拉伸應(yīng)變ISO 527-2/5    屈服, 23°C3.0%ISO 527-2/5    屈服, 60°C4.8%ISO 527-2/5    屈服, 90°C6.0%ISO 527-2/5    屈服, 120°C7.0%ISO 527-2/5    屈服, 150°C7.0%ISO 527-2/5    斷裂, 23°C5.0%ISO 527-2/5    斷裂, 60°C7.0%ISO 527-2/5    斷裂, 90°C9.0%ISO 527-2/5    斷裂, 120°C9.0%ISO 527-2/5    斷裂, 150°C10%ISO 527-2/5沖擊性能額定值單位制測(cè)試方法簡(jiǎn)支梁缺口沖擊強(qiáng)度ISO 179/1eA    -30°C10kJ/m2ISO 179/1eA    -20°C15kJ/m2ISO 179/1eA    23°C20kJ/m2ISO 179/1eA簡(jiǎn)支梁無缺口沖擊強(qiáng)度ISO 179/1eU    -30°C85kJ/m2ISO 179/1eU    -20°C80kJ/m2ISO 179/1eU    23°C75kJ/m2ISO 179/1eU懸壁梁缺口沖擊強(qiáng)度ASTM D256A    -20°C, 3.20 mm140J/mASTM D256A    23°C, 3.20 mm200J/mASTM D256A熱性能額定值單位制測(cè)試方法熱變形溫度    0.45 MPa, 未退火255°CISO 75-2/B    1.8 MPa, 未退火230°CISO 75-2/A連續(xù)使用溫度 290.0°C維卡軟化溫度230°CISO 306/B50線形熱膨脹系數(shù) - 流動(dòng) (30 到 100°C)3.0E-5cm/cm/°CASTM D696注射額定值單位制干燥溫度90.0 到 100°C干燥時(shí)間3.0hr加工（熔體）溫度260 到 290°C模具溫度60.0 到 80.0°C注射速度中等備注1 .at 60 Mpa of cavity pressure2 .20,000 hr這款拉題PA66 15% 玻璃纖維增強(qiáng)材料，是款高抗沖材料