基本性能額定值單位測(cè)試方法比重1.42g/cm3ASTM D792成型收縮率 (Across flow)1.8 to 2.2%ISO 294-4吸水率0.20%ASTM D570熔體質(zhì)量流動(dòng)速率1.7g/10 minASTM D1238    (190℃/2.16kg)1.7g/10 minISO 1133成型收縮率 (flow)1.8 to 2.2%ASTM D955, ISO 294-4吸水率 (24hr)0.20%ASTM D570洛氏硬度ASTM D785    (M-Scale)94    (R-Scale)120機(jī)械性能額定值單位測(cè)試方法拉伸模量2900MPaISO 527-2拉伸應(yīng)力    (Yield)69.0MPaISO 527-267.0MPaASTM D638拉伸伸長率    (Break)85%ASTM D638    (Break)70%ISO 527-2彎曲模量2740MPaASTM D790彎曲強(qiáng)度96.0MPaASTM D790泰伯磨耗量 (1000次)13.0mgASTM D1044夏比缺口沖擊強(qiáng)度 (23°C)15kJ/m2ISO 179/1eAIZOD缺口沖擊強(qiáng)度127J/mASTM D256熱性能額定值單位測(cè)試方法熱畸變溫度ASTM D648    (0.45MPa,未退火)172°C    (1.8MPa,未退火)130°C    (0.45MPa,未退火)163°C    (1.8MPa,未退火)95.0°C線性熱膨脹系數(shù) (flow)0.00010cm/cm/°CASTM E831其它性能額定值單位測(cè)試方法阻燃等級(jí)HBUL 94